Jinan Tieyi guardrail refers to the zinc steel fence made of zinc alloy material. Due to its high strength, high hardness, exquisite appearance, bright color and other advantages, it has become the mainstream product used in residential areas and field fences.

傳統(tǒng)的護(hù)欄使用鐵條、鋁合金材料，需要借助電焊等工藝技術(shù)，而且質(zhì)地較軟、容易生銹、色彩單一。鋅鋼護(hù)欄完美地解決了傳統(tǒng)護(hù)欄的缺點(diǎn)，而且價(jià)格低廉，成為傳統(tǒng)陽(yáng)臺(tái)護(hù)欄材料的替代產(chǎn)品。

Traditional guardrails use iron bars and aluminum alloy materials, which need the help of welding and other technology, and have soft texture, easy to rust and single color. Zinc steel guardrail perfectly solves the shortcomings of traditional guardrail, and the price is low. It has become an alternative to traditional balcony guardrail materials.

（一）材料

（1） Materials

鐵藝護(hù)欄由基材和配件組成。

Iron guardrail is composed of base material and accessories.

鐵藝護(hù)欄型材 鐵藝護(hù)欄的基材為高溫?zé)峤\材料，熱浸鋅是指把優(yōu)質(zhì)鋼材投入幾千度的鋅液池中，浸泡達(dá)一定時(shí)間以后鋅液就會(huì)滲透到鋼材中，使之形成一種特殊的鋅鋼合金，熱浸鋅材料表面不經(jīng)任何處理在野外環(huán)境中即可達(dá)30年不銹蝕，如：高速公路護(hù)欄、高壓電塔都是采用高溫?zé)峤\材料，其防銹長(zhǎng)達(dá)30年之久，徹底解決了多年來(lái)防銹、美觀(guān)與安全之間的問(wèn)題。

The base material of iron guardrail profile iron guardrail is high-temperature hot-dip galvanizing material. Hot dip galvanizing refers to putting high-quality steel into a zinc bath with thousands of degrees. After soaking for a certain time, the zinc will penetrate into the steel to form a special zinc steel alloy. Without any treatment, the surface of hot-dip galvanizing material will not rust for 30 years in the field environment, such as highway guardrail High voltage electric towers are made of high-temperature hot-dip galvanized materials, which have been rustproof for 30 years, completely solving the problems between rust prevention, beauty and safety for many years.

鐵藝護(hù)欄配件采用使用壽命可達(dá)50年之久的改性高強(qiáng)度工程尼龍，其強(qiáng)度、硬度遠(yuǎn)高于普通鋼制材料，每平方米可承受183MPA以上的壓力，2729MPA的拉伸力，可承受220℃以下高溫不變形等優(yōu)點(diǎn)。

Iron guardrail accessories adopt modified high-strength engineering nylon with a service life of up to 50 years. Its strength and hardness are much higher than ordinary steel materials. It can withstand the pressure of more than 183mpa and the tensile force of 2729mpa per square meter, and can withstand the high temperature below 220 ℃ without deformation.

（二）工藝

（2） Craft

１、鐵藝護(hù)欄工藝：采用無(wú)焊連接、橫豎穿插組裝而成。相對(duì)于傳統(tǒng)的鐵藝護(hù)欄，安裝更加快捷，外表更加美觀(guān)。

1. Iron guardrail Technology: it is assembled by non welding connection and horizontal and vertical interspersed assembly. Compared with the traditional iron guardrail, the installation is faster and the appearance is more beautiful.

２、鐵藝護(hù)欄的基材由六層組成，分別是：

2. The base material of iron guardrail consists of six layers:

(1)鋼材層(Base steel)：基材，硬度值為159DPN；

(1) Base steel: base material with hardness value of 159dpn;

(2)鋅鋼合金層(Zeta layer)：更靠近基材的一層致密合金層，構(gòu)造復(fù)雜，耐腐蝕性極強(qiáng)，以FeZn7及FeZn13化合存在，硬度值為211DPN，含F(xiàn)e為7%-11%；

(2) Zinc steel alloy layer: a dense alloy layer closest to the substrate, with complex structure and strong corrosion resistance. It exists in the combination of fezn7 and fezn13, with hardness value of 211dpn and Fe content of 7% - 11%;

(3)亞鉛層(Delta layer)：顯著單斜系柱狀組織，F(xiàn)e含量為6%，無(wú)毒，耐腐蝕，硬度值為179DPN；

(3) Delta layer: significant monoclinic columnar structure, Fe content of 6%, non-toxic, corrosion-resistant, hardness value of 179dpn;

(4)純鋅層(Eta layer)：稠密六方晶系，變形加工不易破裂，鋅純度98.5%，硬度值為70DPN；

(4) ETA layer: dense hexagonal crystal system, which is not easy to crack after deformation. The purity of zinc is 98.5% and the hardness value is 70dpn;

(5)高鋅磷化層：具有良好的耐腐蝕性，并增強(qiáng)涂膜與基材附著力；

(5) High zinc phosphating layer: it has good corrosion resistance and enhances the adhesion between the film and the substrate;

(6)阿克蘇——諾貝爾彩色離分子高溫固化層：優(yōu)異的防腐性能及抗撞擊性能，具有的抗紫外、抗氧化和表面自潔性能，色澤變化率15年不超過(guò)5%。

(6) Akzo Nobel color ionomer high temperature curing layer: excellent corrosion resistance and impact resistance, excellent UV resistance, oxidation resistance and surface self-cleaning performance, and the color change rate shall not exceed 5% in 15 years.